Optimization of the Co–Pi/α-Fe2O3 Catalyst Synthesis Parameters Using the Taguchi Method for Water-Splitting Application

 Masoud Toghraei Masoud Toghraei ,  Hossein Siadati Hossein Siadati
Российский электрохимический журнал
Abstract / Full Text

The use of hematite as a photoanode has been limited due to its optoelectronic properties and a large overpotential for photo-assisted water splitting. In this study, a cobalt-phosphate (Co–Pi) layer was deposited on hematite photoanodes (α-Fe2O3) in order to increase the lifetime of the photogenerated holes and to lower the applied bias. The influence of the Co–Pi catalyst thickness, the pH of deposition, and the scan rate of the photoelectrochemical (PEC) measurements were optimized using the Taguchi statistical method. An L9 orthogonal array, with the three factors of control at three levels, was employed to determine the optimum conditions for water splitting of neutral water with minimum applied bias. After depositing Co‒Pi layer on the α-Fe2O3 at different conditions, the PEC was measured via the linear sweep voltammetry (LSV) and chronoamperometry. The analysis of variance of the mean overpotential in comparison with the bare hematite and the signal-to-noise ratio indicated the great influence of catalyst thickness on the decreasing of overpotential for photo-assisted water splitting in comparison with the bare α-Fe2O3. The characterization of the catalyst and the α-Fe2O3 morphology were carried out by SEM, XRD, and EDS. The optimized photoanode showed an enhancement of around two times for photocurrent and 1.5 times in incident photon-to-current conversion efficiency (IPCE) compared to the bare α-Fe2O3. These findings result in an understanding of the role of the Co–Pi catalyst role in improving the hematite photoanode.

Author information
  • Material Science and Engineering Department; K.N. Toosi University of Technology, Vanak Square, Tehran, Iran

    Masoud Toghraei &  Hossein Siadati

  1. Vayssieres, L., On Solar Hydrogen and Nanotechnology, John Wiley & Sons, 2010.
  2. Kim, J.Y., et al., Single-crystalline, wormlike hematite photoanodes for efficient solar water splitting, Sci. Rep., 2013, vol. 3, p. 2681.
  3. Fujishima, A., Electrochemical photolysis of water at a semiconductor electrode, Nature, 1972, vol. 238, p. 37.
  4. Zhong, D.K. and Gamelin, D.R., Photoelectrochemical water oxidation by cobalt catalyst (“Co−Pi”)/α-Fe2O3 composite photoanodes: oxygen evolution and resolution of a kinetic bottleneck, J. Am. Chem. Soc., 2010, vol. 132, p. 4202.
  5. Sivula, K., Le Formal, F., and Grätzel, M., Solar water splitting: progress using hematite (α-Fe2O3) photoelectrodes, Chem. Sus. Chem., 2011, vol. 4, p. 432.
  6. Carroll, G.M., Zhong, D.K., and Gamelin, D.R., Mechanistic insights into solar water oxidation by cobalt-phosphate-modified α-Fe2O3 photoanodes, Energy Environ. Sci., 2015, vol. 8, p. 577.
  7. Shinar, R. and Kennedy, J.H., Photoactivity of doped α-Fe2O3 electrodes, Solar Energy Mater., 1982, vol. 6, no. 3, p. 323.
  8. Zhong, D.K., et al., Photo-assisted electrodeposition of cobalt-phosphate (Co-Pi) catalyst on hematite photoanodes for solar water oxidation, Energy Environ. Sci., 2011, vol. 4, no. 5, p. 1759.
  9. Kay, A., Cesar, I., and Grätzel, M., New benchmark for water photooxidation by nanostructured α-Fe2O3 films, J. Am. Chem. Soc., 2006, vol. 128, no. 49, p. 15714.
  10. McDonald., K.J. and Choi, K.S., Photodeposition of Co-based oxygen evolution catalysts on α-Fe2O3 photoanodes, Chem. Mater., 2011, vol. 23, no. 7, p. 1686.
  11. Van de Krol, R. and Grätzel, M., Photoelectrochemical Hydrogen Production, Springer, 2011.
  12. Hamann, T.W., Splitting water with rust: hematite photoelectrochemistry, Dalton Trans., 2012, vol. 41, no. 26, p. 7830.
  13. Barroso, M., et al., The role of cobalt phosphate in enhancing the photocatalytic activity of α-Fe2O3 toward water oxidation, J. Am. Chem. Soc., 2011, vol. 133, no. 38, p. 14868.
  14. Barroso, M., et al., Dynamics of photogenerated holes in surface modified α-Fe2O3 photoanodes for solar water splitting, Proc. Nat. Acad. Sci., 2012, vol. 109, no. 39, p. 15640.
  15. Lin, F. and Boettcher, S.W., Adaptive semiconductor/electrocatalyst junctions in water-splitting photoanodes, Nature Mater., 2014, vol. 13, no. 1, p. 81.
  16. Roy, R.K., A Primer on the Taguchi Method, Society of Manufacturing Engineers, 1990.
  17. Schrebler, R., et al., An electrochemical deposition route for obtaining α-Fe2O3 thin films, Electrochem. Solid State Lett., 2006. vol. 9, no. 7, p. C110.
  18. Hamann, C., Hamnett, H.A., and Vielstich, W., Electrochemistry, John Wiley & Sons, 1998.
  19. Gerken, J.B., et al., Electrochemical water oxidation with cobalt-based electrocatalysts from pH 0–14: the thermodynamic basis for catalyst structure, stability, and activity, J. Am. Chem. Soc., 2011, vol. 133, no. 36, p. 14431.
  20. Shi, X., Zhang, K., and Park, J.H., Understanding the positive effects of (Co–Pi) co-catalyst modification in inverse-opal structured α-Fe2O3-based photoelectrochemical cells, Int. J. Hydrogen Energy, 2013. vol. 38, no. 29, p. 12725.
  21. Kanan, M.W., Surendranath, Y., and Nocera, D.G., Cobalt–phosphate oxygen-evolving compound, Chem. Soc. Rev., 2009, vol. 38, no. 1, p. 109.
  22. Enache, C., Liang, Y., and Van de Krol, R., Characterization of structured α-Fe2O3 photoanodes prepared via electrodeposition and thermal oxidation of iron, Thin Solid Films, 2011, vol. 520, no. 3, p. 1034.
  23. Bak, A., Choi, W., and Park, H., Enhancing the photoelectrochemical performance of hematite (α-Fe2O3) electrodes by cadmium incorporation, Appl. Catal. B: Environ., 2011, vol. 110, p. 207.
  24. Kanan, M.W. and Nocera, D.G., In situ formation of an oxygen-evolving catalyst in neutral water containing phosphate and Co2+, Science, 2008, vol. 321, no. 5892, p. 1072.
  25. Surendranath, Y., Kanan, M.W., and Nocera, D.G., Mechanistic studies of the oxygen evolution reaction by a cobalt-phosphate catalyst at neutral pH, J. Am. Chem. Soc., 2010, vol. 132, no. 46, p. 16501.
  26. Lutterman, D.A., Surendranath, Y., and Nocera, D.G., A self-healing oxygen-evolving catalyst, J. Am. Chem. Soc., 2009, vol. 131, no. 11, p. 3838.
  27. Surendranath, Y., Dinca, M., and Nocera, D.G., Electrolyte-dependent electrosynthesis and activity of cobalt-based water oxidation catalysts, J. Am. Chem. Soc., 2009, vol. 131, no. 7, p. 2615.
  28. Steinmiller, E.M. and Choi, K.-S., Photochemical deposition of cobalt-based oxygen evolving catalyst on a semiconductor photoanode for solar oxygen production, Proc. Nat. Acad. Sci., 2009, vol. 106, no. 49, p. 20633.
  29. Wang, L., Lee, C.-Y., and Schmuki, P., Influence of annealing temperature on photoelectrochemical water splitting of α-Fe2O3 films prepared by anodic deposition, Electrochim. Acta, 2013, vol. 91, p. 307.
  30. Spray, R.L. and Choi, K.-S., Photoactivity of transparent nanocrystalline α-Fe2O3 electrodes prepared via anodic electrodeposition, Chem. Mater., 2009, vol. 21, no. 15, p. 3701.
  31. Zhong, D.K., et al., Solar water oxidation by composite catalyst/α-Fe2O3 photoanodes, J. Am. Chem. Soc., 2009, vol. 131, no. 17, p. 6086.
  32. Tilley, S.D., et al., Light-induced water splitting with hematite: improved nanostructure and iridium oxide catalysis, Angew. Chem., 2010, vol. 122, no. 36, p. 6549.
  33. Smith, R.D., et al., Photochemical route for accessing amorphous metal oxide materials for water oxidation catalysis, Science, 2013, vol. 340, no. 6128, p. 60.
  34. Bak, T., et al., Photo-electrochemical hydrogen generation from water using solar energy, materials-related aspects, Int. J. Hydrogen Energy, 2002, vol. 27, no. 10, p. 991.